Ten common causes for inferior artificial grass

     The causes of grass fiber color to fade

  • The quality of artificial lawnis not up to standard, such as too little addition of anti- UV agent and anti-aging agent.
  • The formula of grass fiber is not scientific, and some additives of poor quality.
  • Backward production equipment, poor technology and unstable physical properties of artificial grass fiber.
  • Adverse environmental impacts, such as strong ultraviolet radiation in some areas, acid rain corrosion and industrial pollution, etc.ls on site, resulting in visual chromatic aberration.
  • The foundation of the site is uneven with obvious marks on theThe causes of fuzz, pill and pulverization of grass fibers
  • Because of the high frequency of use ofschools, it is more likely for the grass fibers to split into 50-60 filaments. The poor quality of mesh fibers can occur in one to two years.
  • PP fiber is hard and fragile, so it is easy to fuzz and pill.

      The causes of grass fiber shedding

  • Poor production technology, poor quality of artificial straw cloth and glue, resulting in poor binding force of grass.
  • The use of substandard auxiliary materials (quartz sand particles are too large, not round), damage to the grass.

     The causes of rot and cracking at the bottom of artificial grass

  • The bottom of artificial grass is thin,and PP material of general quality is adopted.
  • The glue used at the bottom is of poor quality or poor gluing process, and is too thick.
  • Uneven site foundation is unqualified foundation, which causes great damage to the base cloth of artificial grass.
  • The whole foundation is poorly drained, and the base cloth is immersed in water for a long time.

     The causes for the inconsistent color of artificial grass

  • Poor quality, uneven thickness and unstable color of artificial grass fiber.
  • Poor site installation design, uneven filling of auxiliary materia joints.
  • Unqualified auxiliary materials and contaminated surface layer.

     The causes for uneven interface & large gap

  • The site foundation is not in accordance with the standard requirements, resulting in uneven interface.
  • The joint technology of artificial grass is not good, resulting in uneven.
  • The production technology and quality problems of artificial grass cause deformation, which cannot be straightened, resulting in gaps.
  • Lack of professional construction experience, special construction tools and qualified skilled technicians.

     The causes why the field is black with surface messy

  • Excessive or unqualified colloidal particles used in the site cause large area of black pollution.
  • The artificial grass falls off at local multi-point areas, leaving only the filling materials.
  • Lack of professional construction experience, special tools and qualified skilled technicians.
  • Lack of necessary maintenance after construction.

     The causes for hardening

  • The foundation is not smooth, easy to accumulate water and soak for a long time.
  • The use of quartz sand and other accessories are too fine or uneven thickness.
  • The rubber particles, quartz sand and other auxiliary materials used have too many impurities or large mud content.
  • The artificial grass has poor quality, is not elastic and easy to lose hair, and lacks necessary maintenance.

     The causes for uneven surface of the site

  • The foundation of the artificial grassland is not smooth.
  • Uneven filling and punching of auxiliary materials; And in the construction process, part of the grass seedlings were covered by filler.
  • Artificial grass production technology is not professional, there is a large grass high error.
  • Lack of professional construction experience, special construction tools and qualified skilled technicians.

     The causes for water accumulation occurred in the field

  • Uneven foundation, low place easy water.
  • Lack of maintenance results in site hardening and poor drainage.
  • Local grass fibers are badly worn and open into potholes.
  • Unreasonable filling materials.